NORGLIDE® SMTL Bearings
For improved load capabilities while reducing tolerance compensation.
NORGLIDE® SMTL is a composite material of compounded PTFE, bronze stretched metal and steel backing. In contrast to NORGLIDE® SM, the bronze stretched metal in NORGLIDE® SMTL is separately precompressed and the PTFE compound tape is thinner, which improves load capabilities while reducing tolerance compensation compared to NORGLIDE® SM. Bearings of 0.75 mm of wall thickness or bigger can be produced with an interference fit in the housing. Various methods are available to protect the steel shell from corrosion.
These bearings can also be designed without play. Bearings of 1 mm of wall thickness or greater can be produced with an interference fit in the housing. Various methods are available to protect the steel shell from corrosion.
Availability
The standard PTFE compound contains either EKONOL® graphite or carbon and graphite. Special PTFE compounds are available on request. Fabricated parts include die-cuts, rolled cylinders, flanged cylinders and deep-drawn bearings.
Standard Thickness
NORGLIDE® SMTL-Type
|
|
| Nominal thickness (mm) | Material Structure |
| CuSn6 / Stretched Metal Steel Backing |
|
| 0.50 | • |
| 0.75 | • |
| 1.0 | • |
Related Characteristics
NORGLIDE® SMTL, Type SMTL050EG-3036-B
|
|||
| Maximum permissible specific bearing load --Static --Dynamic |
SG PL 0044 | 240 to 300 170 |
N/mm2 |
| Coefficient of friction at RT
--On steel with ≥ 58 HRC |
@ 4.8 MPa and 0.058 m/s @ 70 MPa and 0.0065 m/s SG PL 0003 |
0.15 0.10 |
|
| Deformation under load | 23ºC @ 100 N/mm 2, 1h
SG PL 0015 |
≤ 15 | µm |
| Maximum continuous operating temperature | 180 | ºC | |
| K Factor | @ RT on steel with ≥ 58 HRC
SG PL 0003 |
0.10 | 10-6 mm3/ Nm |
| Note: The above mentioned performance values were measured in laboratory tests and must not be considered as a specification for design. | |||
Find out about NORGLIDE® H.