Maintenance-free bearing with metal backing
| NORGLIDE® T is a composite material of compounded PTFE tape on a metal shell. This material structure enables machining of the bearing in the housing--which is an alternative to the sizing process--to obtain tightest tolerances on the inside diameter.
The very thick PTFE layer isolates noise and allows to design bearings without play. Bearings of more than 0.75 mm thickness can be produced with an interference fit in the housing. Various methods are available to protect the steel shell from corrosion.
Availability
The standard PTFE compound contains carbon and graphite. Special PTFE compounds are available on request. Fabricated parts include rolled bearings with or without an axial flange, deep-drawn bearings and die-cuts. The metal backing is available in steel, aluminum or stainless for use in chemically-harsh environments.
|
NORGLIDE® T-Type
Standard Thickness Table
|
| Nom Thickness (mm) |
Material Structure |
| Steel |
Steel 1.4401 |
Alu |
| 0.50 |
|
|
|
| 0.75 |
|
|
|
| 1.00 |
|
|
|
| |
1.50 |
|
|
|
|
NORGLIDE® T, Type T100CG-4064-B
Related Characteristics
|
| Maximum permissible specific bearing load static |
|
180 |
MPa |
| bearing load dynamic |
|
150 |
MPa |
| Coefficient of friction at RT |
@ 4.8 MPa and 0.058 m/s |
0.130 |
|
| on steel with ≥ 58 HPX |
@ 70 MPa and 0.0065 m/s |
0.065 |
|
| Deformation under load |
23ºC @ 100 N/mm 2, 1h |
≤ 30 |
micron |
| Coefficient of heat transmission |
SG PA 3022 |
2100 |
W/m2K |
| Operating temperature range |
continuous |
-200 to +180 |
ºC |
| |
intermittent |
260 |
ºC |
| Coefficient of linear thermal expansion |
SG PA 1025 |
8 |
10-5/K |
| K Factor |
|
0.21 |
10-6 mm3/ Nm |
| Volume resistivity |
SG PA 1081 |
³ 105
|
Ωcm2
|